| CAS: | 123-77-3 |
| 分子式: | C2H4N4O2 |
| 分子量: | 116.08 |
| 熔点: | 225-226℃ |
| 闪点: | 225 °C |
| 沸点: | 217.08 °C |
| 密度: | 1.65 g/cm3 |
| 中文名称: | | 偶氮双甲酰胺 | | 二氮烯二甲酰胺 | | 偶氮二甲酰胺 | | 发泡剂AC | | 发泡剂ADC |
|
| 英文名称: | | Diazenedicarboxamide | | Azodiformamide | | Azodicarbonamide | | 1,1'-azobis-formamid | | 1,1'-azobis(formamide) | | 1,1'-azobiscarbamide | | 1,1'-azobisformamide | | 1,1'-azodiformamide | | 1,1-azobisformamide | | abfa | | az | | azobiscarbonamide | | azobiscarboxamide | | azodicarbamide | | azodicarboamide | | azodicarboxamide | | azodicarboxylic acid diamide | | celogen az | | celogen az 130 | | celogen az 199 | | celosen az | | chkhz 21 | | chkhz 21R | | delta(1,1')-biurea | | ficel ep-a | | genitron ac | | genitron ac 2 | | genitron ac 4 | | genitron epc | | kempore | | kempore 125 | | kempore 60/40 | | kempore r 125 | | lucel ada | | nci-c55981 | | nitropore | | pinhole acr 3 | | pinhole ak 2 | | poramid k 1 | | porofor 505 | | porofor adc/r | | porofor chkhz 21 | | porofor chkhz 21R | | porofor-lk 1074 (bayer) | | unifoam az | | unifoam azh 25 | | uniform az | | yunihomu az |
|
| 性质描述: | 该品为白色或淡黄色粉末。熔点>180℃（分解），相对密度为1.66(20/4℃)。溶于碱，不溶于酸、醇、汽油、苯、吡啶和水。120℃以上易分解，放出大量氮气，在密闭容器中易造成爆炸事故。在室温下贮存甚稳定，对设备无腐蚀作用。具有自熄性。与硫化促进剂和橡胶、塑料的其他配合剂无反应。Ba， Cd， Pb， Zn的有机盐类，可溶性的亚硝酸盐和硫氧酸盐能促进其分解。当加入氨、丙三醇和尿素衍生物时，会降低其分解温度。 |
| 生产方法: | 工业生产发泡剂AC，由水合肼、尿素与硫酸缩合成中间体联二脲，再经氧化而得成品。1.缩合将尿素溶于2%水合肼溶液，加到反应锅。在搅拌下加硫酸使料液pH值达到1-2，加热，使pH值转为2-5，再缓缓加入硫酸，保持pH值2-5反应数小时后，取样测定终点（用0.1N碘溶液滴定含肼量）。缩合成的联二脲，滤出硫酸铵母液后，用热水洗涤，供氧化工序用。2.氧化将联二脲放入反应锅用水溶解，加入溴化钠，通入氯气，反应温度控制在30-50℃，制得的偶氮二甲酰胺先用温水洗至中性，经离心机甩干干燥后，得成品。氧化工序对发泡剂AC的产品质量和生产本影响最大。早期采用硝酸法和铬酸法，由于成本和污染的原因，已趋于淘汰。氯气-溴为氧化剂取代铬盐氧化联二脲生产发泡剂AC的方法，使产品成本降低很多。其他的方法还有：有空气和二氧化氮处理联二脲，收率为84.3%；用电解法生产发泡剂AC；采用过氧化氢氧化联二脲的方法。原料消耗定额：水合肼（40%）1160kg/t、尿素（含氮量≥46%）1330kg/t、液氯800kg/t、烧碱（30%）2000kg/t、硫酸（98%）1140kg/t。 |
| 用途: | 通用型发气量大的发泡剂。广泛用于聚氯乙烯、聚乙烯、乙烯-乙酸乙烯共聚物、聚丙烯、聚苯乙烯、ABS、尼龙-6和氯丁橡胶等多种合成材料，至今还没有能与竞争的产品出现。在这些应用领域中，聚乙烯用量占25-30%，聚氯乙烯用量占15-20%。 |